Viscosity measurements of nanofluids at elevated temperatures and pressures

Anoop Baby, Khalifa Taimour, Mohammed Al-Jubouri, Reza Sadr, Mahmood Amani

Research output: Chapter in Book/Report/Conference proceedingConference contribution

1 Citation (Scopus)

Abstract

Engineered colloidal suspensions of nano-sized particles (less than 100nm) dispersed in a base fluid (nanofluid), have shown potential for industrial cooling fluids due to their enhanced heat transfer characteristics. Understanding the rheological characteristics of these suspensions is vital while employing them for flow applications. The effect of temperature on the viscosity of nanofluids at atmospheric pressure is well documented in literatures; however, there are no available data for viscosity measurements of nanofluids at elevated pressure and temperature. In this work, rheological characteristics of oil based nanofluids at high pressures and temperatures, order of 100atm and 100°C, respectively, are investigated. Nanofluid is prepared by dispersing commercially available SiO2 nanoparticles (∼20nm) in a highly refined paraffinic mineral oil (Therm Z-32, QALCO QATAR) which has wide applications for heat exchangers in oil industry. The rheological characteristics of both the base fluid and the nanofluid are measured using a High Pressure High Temperature (HPHT) viscometer. During experimentation, viscosity values are measured at pressures varying from 10MPa to 40MPa and temperatures ranging from 25°C to 170°C for nanofluid with mass concentrations of 3 percent. The viscosity values of nanofluids as well as base fluid are observed to increase with the increase in pressure. From the pressure coefficient values evaluated for basefluid and nanofluid, it is evident that the effect of pressure on nanofluid and basefluid was similar with no additional effect with respect to particle loading.

Original languageEnglish
Title of host publicationASME 2013 11th International Conference on Nanochannels, Microchannels and Minichannels, ICNMM 2013
DOIs
Publication statusPublished - 2013
EventASME 2013 11th International Conference on Nanochannels, Microchannels and Minichannels, ICNMM 2013 - Sapporo, Japan
Duration: 16 Jun 201319 Jun 2013

Other

OtherASME 2013 11th International Conference on Nanochannels, Microchannels and Minichannels, ICNMM 2013
CountryJapan
CitySapporo
Period16/6/1319/6/13

Fingerprint

Nanofluid
Viscosity measurement
Viscosity
Fluids
Temperature
Fluid
Suspensions
Oils
Mineral Oil
Viscometers
Mineral oils
Atmospheric pressure
Heat exchangers
Colloidal Suspensions
Heat Exchanger
SiO2
Nanoparticles
Heat transfer
Cooling
Experimentation

ASJC Scopus subject areas

  • Fluid Flow and Transfer Processes
  • Process Chemistry and Technology
  • Modelling and Simulation

Cite this

Baby, A., Taimour, K., Al-Jubouri, M., Sadr, R., & Amani, M. (2013). Viscosity measurements of nanofluids at elevated temperatures and pressures. In ASME 2013 11th International Conference on Nanochannels, Microchannels and Minichannels, ICNMM 2013 [V001T11A003] https://doi.org/10.1115/ICNMM2013-73103

Viscosity measurements of nanofluids at elevated temperatures and pressures. / Baby, Anoop; Taimour, Khalifa; Al-Jubouri, Mohammed; Sadr, Reza; Amani, Mahmood.

ASME 2013 11th International Conference on Nanochannels, Microchannels and Minichannels, ICNMM 2013. 2013. V001T11A003.

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Baby, A, Taimour, K, Al-Jubouri, M, Sadr, R & Amani, M 2013, Viscosity measurements of nanofluids at elevated temperatures and pressures. in ASME 2013 11th International Conference on Nanochannels, Microchannels and Minichannels, ICNMM 2013., V001T11A003, ASME 2013 11th International Conference on Nanochannels, Microchannels and Minichannels, ICNMM 2013, Sapporo, Japan, 16/6/13. https://doi.org/10.1115/ICNMM2013-73103
Baby A, Taimour K, Al-Jubouri M, Sadr R, Amani M. Viscosity measurements of nanofluids at elevated temperatures and pressures. In ASME 2013 11th International Conference on Nanochannels, Microchannels and Minichannels, ICNMM 2013. 2013. V001T11A003 https://doi.org/10.1115/ICNMM2013-73103
Baby, Anoop ; Taimour, Khalifa ; Al-Jubouri, Mohammed ; Sadr, Reza ; Amani, Mahmood. / Viscosity measurements of nanofluids at elevated temperatures and pressures. ASME 2013 11th International Conference on Nanochannels, Microchannels and Minichannels, ICNMM 2013. 2013.
@inproceedings{e75b8a94a22c4d84a904d83bab8e6b54,
title = "Viscosity measurements of nanofluids at elevated temperatures and pressures",
abstract = "Engineered colloidal suspensions of nano-sized particles (less than 100nm) dispersed in a base fluid (nanofluid), have shown potential for industrial cooling fluids due to their enhanced heat transfer characteristics. Understanding the rheological characteristics of these suspensions is vital while employing them for flow applications. The effect of temperature on the viscosity of nanofluids at atmospheric pressure is well documented in literatures; however, there are no available data for viscosity measurements of nanofluids at elevated pressure and temperature. In this work, rheological characteristics of oil based nanofluids at high pressures and temperatures, order of 100atm and 100°C, respectively, are investigated. Nanofluid is prepared by dispersing commercially available SiO2 nanoparticles (∼20nm) in a highly refined paraffinic mineral oil (Therm Z-32, QALCO QATAR) which has wide applications for heat exchangers in oil industry. The rheological characteristics of both the base fluid and the nanofluid are measured using a High Pressure High Temperature (HPHT) viscometer. During experimentation, viscosity values are measured at pressures varying from 10MPa to 40MPa and temperatures ranging from 25°C to 170°C for nanofluid with mass concentrations of 3 percent. The viscosity values of nanofluids as well as base fluid are observed to increase with the increase in pressure. From the pressure coefficient values evaluated for basefluid and nanofluid, it is evident that the effect of pressure on nanofluid and basefluid was similar with no additional effect with respect to particle loading.",
author = "Anoop Baby and Khalifa Taimour and Mohammed Al-Jubouri and Reza Sadr and Mahmood Amani",
year = "2013",
doi = "10.1115/ICNMM2013-73103",
language = "English",
isbn = "9780791855591",
booktitle = "ASME 2013 11th International Conference on Nanochannels, Microchannels and Minichannels, ICNMM 2013",

}

TY - GEN

T1 - Viscosity measurements of nanofluids at elevated temperatures and pressures

AU - Baby, Anoop

AU - Taimour, Khalifa

AU - Al-Jubouri, Mohammed

AU - Sadr, Reza

AU - Amani, Mahmood

PY - 2013

Y1 - 2013

N2 - Engineered colloidal suspensions of nano-sized particles (less than 100nm) dispersed in a base fluid (nanofluid), have shown potential for industrial cooling fluids due to their enhanced heat transfer characteristics. Understanding the rheological characteristics of these suspensions is vital while employing them for flow applications. The effect of temperature on the viscosity of nanofluids at atmospheric pressure is well documented in literatures; however, there are no available data for viscosity measurements of nanofluids at elevated pressure and temperature. In this work, rheological characteristics of oil based nanofluids at high pressures and temperatures, order of 100atm and 100°C, respectively, are investigated. Nanofluid is prepared by dispersing commercially available SiO2 nanoparticles (∼20nm) in a highly refined paraffinic mineral oil (Therm Z-32, QALCO QATAR) which has wide applications for heat exchangers in oil industry. The rheological characteristics of both the base fluid and the nanofluid are measured using a High Pressure High Temperature (HPHT) viscometer. During experimentation, viscosity values are measured at pressures varying from 10MPa to 40MPa and temperatures ranging from 25°C to 170°C for nanofluid with mass concentrations of 3 percent. The viscosity values of nanofluids as well as base fluid are observed to increase with the increase in pressure. From the pressure coefficient values evaluated for basefluid and nanofluid, it is evident that the effect of pressure on nanofluid and basefluid was similar with no additional effect with respect to particle loading.

AB - Engineered colloidal suspensions of nano-sized particles (less than 100nm) dispersed in a base fluid (nanofluid), have shown potential for industrial cooling fluids due to their enhanced heat transfer characteristics. Understanding the rheological characteristics of these suspensions is vital while employing them for flow applications. The effect of temperature on the viscosity of nanofluids at atmospheric pressure is well documented in literatures; however, there are no available data for viscosity measurements of nanofluids at elevated pressure and temperature. In this work, rheological characteristics of oil based nanofluids at high pressures and temperatures, order of 100atm and 100°C, respectively, are investigated. Nanofluid is prepared by dispersing commercially available SiO2 nanoparticles (∼20nm) in a highly refined paraffinic mineral oil (Therm Z-32, QALCO QATAR) which has wide applications for heat exchangers in oil industry. The rheological characteristics of both the base fluid and the nanofluid are measured using a High Pressure High Temperature (HPHT) viscometer. During experimentation, viscosity values are measured at pressures varying from 10MPa to 40MPa and temperatures ranging from 25°C to 170°C for nanofluid with mass concentrations of 3 percent. The viscosity values of nanofluids as well as base fluid are observed to increase with the increase in pressure. From the pressure coefficient values evaluated for basefluid and nanofluid, it is evident that the effect of pressure on nanofluid and basefluid was similar with no additional effect with respect to particle loading.

UR - http://www.scopus.com/inward/record.url?scp=84892653967&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84892653967&partnerID=8YFLogxK

U2 - 10.1115/ICNMM2013-73103

DO - 10.1115/ICNMM2013-73103

M3 - Conference contribution

SN - 9780791855591

BT - ASME 2013 11th International Conference on Nanochannels, Microchannels and Minichannels, ICNMM 2013

ER -