Etude des propriétés physico-chimiques de ZnRb4(P3O9)2.6H2O

Translated title of the contribution: Study of physicochemical properties of ZnRb4(P3O9)2.6H2O

Ali Abouimrane, K. Sbai, K. El Kababi, A. Lahmidi, A. Atibi, Serge Vilminot

Research output: Contribution to journalArticle

4 Citations (Scopus)

Abstract

The dehydration of ZnRb4(P3O9)2.6H2O was investigated, between 25 and 600°C, by TG-DTA, X-ray diffraction, IR. It leads, between 300 and 500°C, to a mixture of long chain polyphosphates RbPO3 and ZnRb2(PO3)4 which stays stable until its melting point. The IR (1400-30 cm-1) and Raman spectra (1400-100 cm-1) of ZnRb4(P3O9)2.6H2O are reported and assignments of fundamental modes proposed and compared with theoretical results obtained via the MNDO method for P3O9 ring with Cs symmetry. (La déshydratation, sous pression atmosphérique, du cyclotriphosphate ZnRb4(P3O9)2.6H2O, a été effectuée, entre 25 and 600°C, par spectrométrie IR, diffraction des rayons X, ATG et ATD. Elle conduit, entre 300 and 500°C, au mélange de polyphosphates RbPO3 et ZnRb2 (PO3)4 qui reste stable jusqu'à la fusion. Les spectres vibrationnels IR (1400-30 cm-1) et Raman (1400-100 cm-1) du sel étudié ont été interprétés dans le domaine des vibrations de valence et de déformation du cycle P3O9 et comparés avec les résultats des calculs théoriques par la méthode MNDO pour un cycle isolé de symétrie Cs).

Original languageFrench
Pages (from-to)605-619
Number of pages15
JournalPhosphorus, Sulfur and Silicon and Related Elements
Volume177
Issue number3
DOIs
Publication statusPublished - 2002
Externally publishedYes

Fingerprint

Polyphosphates
Vibration
Dehydration
X-Ray Diffraction
Differential thermal analysis
Freezing
Melting point
Raman scattering
Fusion reactions
Diffraction
X ray diffraction

Keywords

  • Cyclotriphosphate
  • IR and Raman spectra
  • Rubidium polyphosphate dehydration
  • ZnRb-salt

ASJC Scopus subject areas

  • Inorganic Chemistry

Cite this

Etude des propriétés physico-chimiques de ZnRb4(P3O9)2.6H2O. / Abouimrane, Ali; Sbai, K.; El Kababi, K.; Lahmidi, A.; Atibi, A.; Vilminot, Serge.

In: Phosphorus, Sulfur and Silicon and Related Elements, Vol. 177, No. 3, 2002, p. 605-619.

Research output: Contribution to journalArticle

Abouimrane, Ali ; Sbai, K. ; El Kababi, K. ; Lahmidi, A. ; Atibi, A. ; Vilminot, Serge. / Etude des propriétés physico-chimiques de ZnRb4(P3O9)2.6H2O. In: Phosphorus, Sulfur and Silicon and Related Elements. 2002 ; Vol. 177, No. 3. pp. 605-619.
@article{9a0788f65af449ee8f942dfd805c105a,
title = "Etude des propri{\'e}t{\'e}s physico-chimiques de ZnRb4(P3O9)2.6H2O",
abstract = "The dehydration of ZnRb4(P3O9)2.6H2O was investigated, between 25 and 600°C, by TG-DTA, X-ray diffraction, IR. It leads, between 300 and 500°C, to a mixture of long chain polyphosphates RbPO3 and ZnRb2(PO3)4 which stays stable until its melting point. The IR (1400-30 cm-1) and Raman spectra (1400-100 cm-1) of ZnRb4(P3O9)2.6H2O are reported and assignments of fundamental modes proposed and compared with theoretical results obtained via the MNDO method for P3O9 ring with Cs symmetry. (La d{\'e}shydratation, sous pression atmosph{\'e}rique, du cyclotriphosphate ZnRb4(P3O9)2.6H2O, a {\'e}t{\'e} effectu{\'e}e, entre 25 and 600°C, par spectrom{\'e}trie IR, diffraction des rayons X, ATG et ATD. Elle conduit, entre 300 and 500°C, au m{\'e}lange de polyphosphates RbPO3 et ZnRb2 (PO3)4 qui reste stable jusqu'{\`a} la fusion. Les spectres vibrationnels IR (1400-30 cm-1) et Raman (1400-100 cm-1) du sel {\'e}tudi{\'e} ont {\'e}t{\'e} interpr{\'e}t{\'e}s dans le domaine des vibrations de valence et de d{\'e}formation du cycle P3O9 et compar{\'e}s avec les r{\'e}sultats des calculs th{\'e}oriques par la m{\'e}thode MNDO pour un cycle isol{\'e} de sym{\'e}trie Cs).",
keywords = "Cyclotriphosphate, IR and Raman spectra, Rubidium polyphosphate dehydration, ZnRb-salt",
author = "Ali Abouimrane and K. Sbai and {El Kababi}, K. and A. Lahmidi and A. Atibi and Serge Vilminot",
year = "2002",
doi = "10.1080/10426500210263",
language = "French",
volume = "177",
pages = "605--619",
journal = "Phosphorus, Sulfur and Silicon and the Related Elements",
issn = "1042-6507",
publisher = "Taylor and Francis Ltd.",
number = "3",

}

TY - JOUR

T1 - Etude des propriétés physico-chimiques de ZnRb4(P3O9)2.6H2O

AU - Abouimrane, Ali

AU - Sbai, K.

AU - El Kababi, K.

AU - Lahmidi, A.

AU - Atibi, A.

AU - Vilminot, Serge

PY - 2002

Y1 - 2002

N2 - The dehydration of ZnRb4(P3O9)2.6H2O was investigated, between 25 and 600°C, by TG-DTA, X-ray diffraction, IR. It leads, between 300 and 500°C, to a mixture of long chain polyphosphates RbPO3 and ZnRb2(PO3)4 which stays stable until its melting point. The IR (1400-30 cm-1) and Raman spectra (1400-100 cm-1) of ZnRb4(P3O9)2.6H2O are reported and assignments of fundamental modes proposed and compared with theoretical results obtained via the MNDO method for P3O9 ring with Cs symmetry. (La déshydratation, sous pression atmosphérique, du cyclotriphosphate ZnRb4(P3O9)2.6H2O, a été effectuée, entre 25 and 600°C, par spectrométrie IR, diffraction des rayons X, ATG et ATD. Elle conduit, entre 300 and 500°C, au mélange de polyphosphates RbPO3 et ZnRb2 (PO3)4 qui reste stable jusqu'à la fusion. Les spectres vibrationnels IR (1400-30 cm-1) et Raman (1400-100 cm-1) du sel étudié ont été interprétés dans le domaine des vibrations de valence et de déformation du cycle P3O9 et comparés avec les résultats des calculs théoriques par la méthode MNDO pour un cycle isolé de symétrie Cs).

AB - The dehydration of ZnRb4(P3O9)2.6H2O was investigated, between 25 and 600°C, by TG-DTA, X-ray diffraction, IR. It leads, between 300 and 500°C, to a mixture of long chain polyphosphates RbPO3 and ZnRb2(PO3)4 which stays stable until its melting point. The IR (1400-30 cm-1) and Raman spectra (1400-100 cm-1) of ZnRb4(P3O9)2.6H2O are reported and assignments of fundamental modes proposed and compared with theoretical results obtained via the MNDO method for P3O9 ring with Cs symmetry. (La déshydratation, sous pression atmosphérique, du cyclotriphosphate ZnRb4(P3O9)2.6H2O, a été effectuée, entre 25 and 600°C, par spectrométrie IR, diffraction des rayons X, ATG et ATD. Elle conduit, entre 300 and 500°C, au mélange de polyphosphates RbPO3 et ZnRb2 (PO3)4 qui reste stable jusqu'à la fusion. Les spectres vibrationnels IR (1400-30 cm-1) et Raman (1400-100 cm-1) du sel étudié ont été interprétés dans le domaine des vibrations de valence et de déformation du cycle P3O9 et comparés avec les résultats des calculs théoriques par la méthode MNDO pour un cycle isolé de symétrie Cs).

KW - Cyclotriphosphate

KW - IR and Raman spectra

KW - Rubidium polyphosphate dehydration

KW - ZnRb-salt

UR - http://www.scopus.com/inward/record.url?scp=18644384817&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=18644384817&partnerID=8YFLogxK

U2 - 10.1080/10426500210263

DO - 10.1080/10426500210263

M3 - Article

VL - 177

SP - 605

EP - 619

JO - Phosphorus, Sulfur and Silicon and the Related Elements

JF - Phosphorus, Sulfur and Silicon and the Related Elements

SN - 1042-6507

IS - 3

ER -