Radiation resistance of advanced ferritic-martensitic steel HCM12A

T. R. Allen, L. Tan, J. D. Tucker, J. Gan, G. Gupta, G. S. Was, S. Shutthanandan, S. Thevuthasan

Research output: Chapter in Book/Report/Conference proceedingChapter

5 Citations (Scopus)

Abstract

HCM12A is an advanced 12 Cr ferritic-martensitic steel designed for higher temperature operation than could be achieved using earlier generation steels such as HT9. HCM12A is one of the advanced alloys under consideration for application in core components in Generation IV nuclear energy systems, and is of particular interest to the supercritical water reactor, sodium fast reactor, and lead fast reactor designs. The radiation resistance of HCM12A has not previously been studied. This work provides information on the hardening and microstructural changes in HCM12A after irradiation using 2.0 MeV protons at 400°C to 10 dpa and 5 MeV Ni-ions at 500°C to 50 dpa. Following irradiation, changes in hardness were measured using Vickers hardness indentation, changes in microstructure and phase stability were studied using transmission electron microscopy, and changes in microchemistry were measured using scanning Auger microscopy. The hardness increases by roughly 70 % and saturates by roughly 5 dpa. The changes to the microstructure contributing to this hardness increase are primarily due to the formation of precipitate phases, with some contribution from changes in dislocation density. Chromium is enriched at grain boundaries prior to irradiation, likely due to grain boundary carbides, and increases further during the irradiation.

Original languageEnglish
Title of host publicationJournal of ASTM International
Pages337-349
Number of pages13
Volume2
Edition8
DOIs
Publication statusPublished - Sep 2005
Externally publishedYes

Fingerprint

Martensitic steel
Steel
Ferritic steel
Hardness
Irradiation
Radiation
Fast reactors
Microchemistry
Grain boundaries
Nuclear Energy
High temperature operations
Microstructure
Phase stability
Vickers hardness
Chromium
Transmission Electron Microscopy
Dislocations (crystals)
Indentation
Nuclear energy
Carbides

Keywords

  • Ferritic-martensitic steel
  • Microstructure
  • Radiation
  • Segregation

ASJC Scopus subject areas

  • Engineering(all)
  • Materials Science(all)
  • Nuclear Energy and Engineering
  • Environmental Engineering
  • Public Health, Environmental and Occupational Health

Cite this

Allen, T. R., Tan, L., Tucker, J. D., Gan, J., Gupta, G., Was, G. S., ... Thevuthasan, S. (2005). Radiation resistance of advanced ferritic-martensitic steel HCM12A. In Journal of ASTM International (8 ed., Vol. 2, pp. 337-349) https://doi.org/10.1520/JAI12382

Radiation resistance of advanced ferritic-martensitic steel HCM12A. / Allen, T. R.; Tan, L.; Tucker, J. D.; Gan, J.; Gupta, G.; Was, G. S.; Shutthanandan, S.; Thevuthasan, S.

Journal of ASTM International. Vol. 2 8. ed. 2005. p. 337-349.

Research output: Chapter in Book/Report/Conference proceedingChapter

Allen, TR, Tan, L, Tucker, JD, Gan, J, Gupta, G, Was, GS, Shutthanandan, S & Thevuthasan, S 2005, Radiation resistance of advanced ferritic-martensitic steel HCM12A. in Journal of ASTM International. 8 edn, vol. 2, pp. 337-349. https://doi.org/10.1520/JAI12382
Allen TR, Tan L, Tucker JD, Gan J, Gupta G, Was GS et al. Radiation resistance of advanced ferritic-martensitic steel HCM12A. In Journal of ASTM International. 8 ed. Vol. 2. 2005. p. 337-349 https://doi.org/10.1520/JAI12382
Allen, T. R. ; Tan, L. ; Tucker, J. D. ; Gan, J. ; Gupta, G. ; Was, G. S. ; Shutthanandan, S. ; Thevuthasan, S. / Radiation resistance of advanced ferritic-martensitic steel HCM12A. Journal of ASTM International. Vol. 2 8. ed. 2005. pp. 337-349
@inbook{1d50a0649cc64574a3da0ac50da6d01b,
title = "Radiation resistance of advanced ferritic-martensitic steel HCM12A",
abstract = "HCM12A is an advanced 12 Cr ferritic-martensitic steel designed for higher temperature operation than could be achieved using earlier generation steels such as HT9. HCM12A is one of the advanced alloys under consideration for application in core components in Generation IV nuclear energy systems, and is of particular interest to the supercritical water reactor, sodium fast reactor, and lead fast reactor designs. The radiation resistance of HCM12A has not previously been studied. This work provides information on the hardening and microstructural changes in HCM12A after irradiation using 2.0 MeV protons at 400°C to 10 dpa and 5 MeV Ni-ions at 500°C to 50 dpa. Following irradiation, changes in hardness were measured using Vickers hardness indentation, changes in microstructure and phase stability were studied using transmission electron microscopy, and changes in microchemistry were measured using scanning Auger microscopy. The hardness increases by roughly 70 {\%} and saturates by roughly 5 dpa. The changes to the microstructure contributing to this hardness increase are primarily due to the formation of precipitate phases, with some contribution from changes in dislocation density. Chromium is enriched at grain boundaries prior to irradiation, likely due to grain boundary carbides, and increases further during the irradiation.",
keywords = "Ferritic-martensitic steel, Microstructure, Radiation, Segregation",
author = "Allen, {T. R.} and L. Tan and Tucker, {J. D.} and J. Gan and G. Gupta and Was, {G. S.} and S. Shutthanandan and S. Thevuthasan",
year = "2005",
month = "9",
doi = "10.1520/JAI12382",
language = "English",
volume = "2",
pages = "337--349",
booktitle = "Journal of ASTM International",
edition = "8",

}

TY - CHAP

T1 - Radiation resistance of advanced ferritic-martensitic steel HCM12A

AU - Allen, T. R.

AU - Tan, L.

AU - Tucker, J. D.

AU - Gan, J.

AU - Gupta, G.

AU - Was, G. S.

AU - Shutthanandan, S.

AU - Thevuthasan, S.

PY - 2005/9

Y1 - 2005/9

N2 - HCM12A is an advanced 12 Cr ferritic-martensitic steel designed for higher temperature operation than could be achieved using earlier generation steels such as HT9. HCM12A is one of the advanced alloys under consideration for application in core components in Generation IV nuclear energy systems, and is of particular interest to the supercritical water reactor, sodium fast reactor, and lead fast reactor designs. The radiation resistance of HCM12A has not previously been studied. This work provides information on the hardening and microstructural changes in HCM12A after irradiation using 2.0 MeV protons at 400°C to 10 dpa and 5 MeV Ni-ions at 500°C to 50 dpa. Following irradiation, changes in hardness were measured using Vickers hardness indentation, changes in microstructure and phase stability were studied using transmission electron microscopy, and changes in microchemistry were measured using scanning Auger microscopy. The hardness increases by roughly 70 % and saturates by roughly 5 dpa. The changes to the microstructure contributing to this hardness increase are primarily due to the formation of precipitate phases, with some contribution from changes in dislocation density. Chromium is enriched at grain boundaries prior to irradiation, likely due to grain boundary carbides, and increases further during the irradiation.

AB - HCM12A is an advanced 12 Cr ferritic-martensitic steel designed for higher temperature operation than could be achieved using earlier generation steels such as HT9. HCM12A is one of the advanced alloys under consideration for application in core components in Generation IV nuclear energy systems, and is of particular interest to the supercritical water reactor, sodium fast reactor, and lead fast reactor designs. The radiation resistance of HCM12A has not previously been studied. This work provides information on the hardening and microstructural changes in HCM12A after irradiation using 2.0 MeV protons at 400°C to 10 dpa and 5 MeV Ni-ions at 500°C to 50 dpa. Following irradiation, changes in hardness were measured using Vickers hardness indentation, changes in microstructure and phase stability were studied using transmission electron microscopy, and changes in microchemistry were measured using scanning Auger microscopy. The hardness increases by roughly 70 % and saturates by roughly 5 dpa. The changes to the microstructure contributing to this hardness increase are primarily due to the formation of precipitate phases, with some contribution from changes in dislocation density. Chromium is enriched at grain boundaries prior to irradiation, likely due to grain boundary carbides, and increases further during the irradiation.

KW - Ferritic-martensitic steel

KW - Microstructure

KW - Radiation

KW - Segregation

UR - http://www.scopus.com/inward/record.url?scp=30744433376&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=30744433376&partnerID=8YFLogxK

U2 - 10.1520/JAI12382

DO - 10.1520/JAI12382

M3 - Chapter

VL - 2

SP - 337

EP - 349

BT - Journal of ASTM International

ER -