Effect of synthesis condition and annealing on the sensitivity and stability of gas sensors made of Zn-doped γ-Fe2O3 particles

Taeyang Kim, Andrew Sharp, Bing Guo

Research output: Contribution to journalArticle

7 Citations (Scopus)

Abstract

Gas sensors made of flame-synthesized Zn-doped γ-Fe2O3 nanoparticles were found to have high sensitivity and high aging resistance. Zinc-doped γ-Fe2O3 nanoparticles and microparticles were synthesized by flame spray pyrolysis (FSP). Gas sensors were fabricated with as-synthesized particles, and with particles that had been annealed. The sensors' response to acetone vapor and H2 was measured as fabricated, and measured again after the sensors were aged for three days. The sensors made from as-synthesized particles showed a gas sensing sensitivity 20 times higher than the literature value. However, sensors made of microparticles lost their sensing ability after three days of aging; sensors made of nanoparticles retained their gas sensing capability after aging. Sensors made of annealed particles did not have significant gas sensing capabilities. Analysis using the William and Hall method showed that the microstrains decreased significantly in both H2/O2 and H2/Air flame synthesized particles after annealing. The results showed that sensors made of flame-synthesized particles have much higher sensitivity than sensors made of particles previously reported. Especially, sensors made of flame-synthesized nanoparticles are resistant towards aging. This aging resistance may be attributed to the particles' ability to retain their microstrains.

Original languageEnglish
Pages (from-to)1003-1009
Number of pages7
JournalKorean Journal of Chemical Engineering
Volume27
Issue number3
DOIs
Publication statusPublished - 2010
Externally publishedYes

Fingerprint

Chemical sensors
Annealing
Sensors
Aging of materials
Nanoparticles
Gases
Spray pyrolysis
Acetone
Zinc
Vapors
Air

Keywords

  • Aging
  • Flame Spray Pyrolysis (FSP)
  • Gas Sensing
  • Microstrains
  • Sensitivity

ASJC Scopus subject areas

  • Chemistry(all)
  • Chemical Engineering(all)

Cite this

Effect of synthesis condition and annealing on the sensitivity and stability of gas sensors made of Zn-doped γ-Fe2O3 particles. / Kim, Taeyang; Sharp, Andrew; Guo, Bing.

In: Korean Journal of Chemical Engineering, Vol. 27, No. 3, 2010, p. 1003-1009.

Research output: Contribution to journalArticle

@article{b11e6df3d91f452aa354367580258d2e,
title = "Effect of synthesis condition and annealing on the sensitivity and stability of gas sensors made of Zn-doped γ-Fe2O3 particles",
abstract = "Gas sensors made of flame-synthesized Zn-doped γ-Fe2O3 nanoparticles were found to have high sensitivity and high aging resistance. Zinc-doped γ-Fe2O3 nanoparticles and microparticles were synthesized by flame spray pyrolysis (FSP). Gas sensors were fabricated with as-synthesized particles, and with particles that had been annealed. The sensors' response to acetone vapor and H2 was measured as fabricated, and measured again after the sensors were aged for three days. The sensors made from as-synthesized particles showed a gas sensing sensitivity 20 times higher than the literature value. However, sensors made of microparticles lost their sensing ability after three days of aging; sensors made of nanoparticles retained their gas sensing capability after aging. Sensors made of annealed particles did not have significant gas sensing capabilities. Analysis using the William and Hall method showed that the microstrains decreased significantly in both H2/O2 and H2/Air flame synthesized particles after annealing. The results showed that sensors made of flame-synthesized particles have much higher sensitivity than sensors made of particles previously reported. Especially, sensors made of flame-synthesized nanoparticles are resistant towards aging. This aging resistance may be attributed to the particles' ability to retain their microstrains.",
keywords = "Aging, Flame Spray Pyrolysis (FSP), Gas Sensing, Microstrains, Sensitivity",
author = "Taeyang Kim and Andrew Sharp and Bing Guo",
year = "2010",
doi = "10.1007/s11814-010-0154-2",
language = "English",
volume = "27",
pages = "1003--1009",
journal = "Korean Journal of Chemical Engineering",
issn = "0256-1115",
publisher = "Springer New York",
number = "3",

}

TY - JOUR

T1 - Effect of synthesis condition and annealing on the sensitivity and stability of gas sensors made of Zn-doped γ-Fe2O3 particles

AU - Kim, Taeyang

AU - Sharp, Andrew

AU - Guo, Bing

PY - 2010

Y1 - 2010

N2 - Gas sensors made of flame-synthesized Zn-doped γ-Fe2O3 nanoparticles were found to have high sensitivity and high aging resistance. Zinc-doped γ-Fe2O3 nanoparticles and microparticles were synthesized by flame spray pyrolysis (FSP). Gas sensors were fabricated with as-synthesized particles, and with particles that had been annealed. The sensors' response to acetone vapor and H2 was measured as fabricated, and measured again after the sensors were aged for three days. The sensors made from as-synthesized particles showed a gas sensing sensitivity 20 times higher than the literature value. However, sensors made of microparticles lost their sensing ability after three days of aging; sensors made of nanoparticles retained their gas sensing capability after aging. Sensors made of annealed particles did not have significant gas sensing capabilities. Analysis using the William and Hall method showed that the microstrains decreased significantly in both H2/O2 and H2/Air flame synthesized particles after annealing. The results showed that sensors made of flame-synthesized particles have much higher sensitivity than sensors made of particles previously reported. Especially, sensors made of flame-synthesized nanoparticles are resistant towards aging. This aging resistance may be attributed to the particles' ability to retain their microstrains.

AB - Gas sensors made of flame-synthesized Zn-doped γ-Fe2O3 nanoparticles were found to have high sensitivity and high aging resistance. Zinc-doped γ-Fe2O3 nanoparticles and microparticles were synthesized by flame spray pyrolysis (FSP). Gas sensors were fabricated with as-synthesized particles, and with particles that had been annealed. The sensors' response to acetone vapor and H2 was measured as fabricated, and measured again after the sensors were aged for three days. The sensors made from as-synthesized particles showed a gas sensing sensitivity 20 times higher than the literature value. However, sensors made of microparticles lost their sensing ability after three days of aging; sensors made of nanoparticles retained their gas sensing capability after aging. Sensors made of annealed particles did not have significant gas sensing capabilities. Analysis using the William and Hall method showed that the microstrains decreased significantly in both H2/O2 and H2/Air flame synthesized particles after annealing. The results showed that sensors made of flame-synthesized particles have much higher sensitivity than sensors made of particles previously reported. Especially, sensors made of flame-synthesized nanoparticles are resistant towards aging. This aging resistance may be attributed to the particles' ability to retain their microstrains.

KW - Aging

KW - Flame Spray Pyrolysis (FSP)

KW - Gas Sensing

KW - Microstrains

KW - Sensitivity

UR - http://www.scopus.com/inward/record.url?scp=77952321955&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=77952321955&partnerID=8YFLogxK

U2 - 10.1007/s11814-010-0154-2

DO - 10.1007/s11814-010-0154-2

M3 - Article

AN - SCOPUS:77952321955

VL - 27

SP - 1003

EP - 1009

JO - Korean Journal of Chemical Engineering

JF - Korean Journal of Chemical Engineering

SN - 0256-1115

IS - 3

ER -