Cobalt oxide functionalized nanoporous carbon electrodes and their excellent supercapacitive performance

Dattatray Dhawale, Gurudas P. Mane, Stalin Joseph, Siddulu N. Talapaneni, Chokkalingam Anand, Ajayan Mano, Salem S. Aldeyab, Kripal S. Lakhi, Ajayan Vinu

Research output: Contribution to journalArticle

9 Citations (Scopus)

Abstract

Nanoporous carbon (CMK-3-150) functionalized with different amounts of cobalt oxide (CoO) nanoparticles was synthesized by an incipient wetness impregnation technique for supercapacitor application. The characterization results reveal that the specific surface area and pore volume of the CoO functionalized CMK-3-150 marginally decrease upon increasing the amount of the CoO whereas the pore diameter and the structure of the CMK-3-150 were not affected even after the functionalization. The electrochemical measurements show that the specific capacitance of the electrodes was enhanced after the functionalization with CoO. Among the electrodes studied, CMK-3-150 functionalized with 15 wt% CoO shows an excellent cycling stability and specific capacitance of 331 F g-1, which is ca. two times higher than that of the pure nanoporous carbon. This enhanced performance is due to the combined contribution of electrical double layer capacitance and pseudocapacitance. A symmetric supercapacitor device based on the CMK-3-150-15Co electrode gives the maximum energy density of 29.67 W h kg-1 at a power density of 0.07 kW kg-1. This journal is

Original languageEnglish
Pages (from-to)13930-13940
Number of pages11
JournalRSC Advances
Volume5
Issue number18
DOIs
Publication statusPublished - 2015
Externally publishedYes

Fingerprint

Cobalt
Carbon
Electrodes
Oxides
Capacitance
Impregnation
Specific surface area
cobalt oxide
Nanoparticles
Supercapacitor

ASJC Scopus subject areas

  • Chemical Engineering(all)
  • Chemistry(all)

Cite this

Dhawale, D., Mane, G. P., Joseph, S., Talapaneni, S. N., Anand, C., Mano, A., ... Vinu, A. (2015). Cobalt oxide functionalized nanoporous carbon electrodes and their excellent supercapacitive performance. RSC Advances, 5(18), 13930-13940. https://doi.org/10.1039/c4ra14041a

Cobalt oxide functionalized nanoporous carbon electrodes and their excellent supercapacitive performance. / Dhawale, Dattatray; Mane, Gurudas P.; Joseph, Stalin; Talapaneni, Siddulu N.; Anand, Chokkalingam; Mano, Ajayan; Aldeyab, Salem S.; Lakhi, Kripal S.; Vinu, Ajayan.

In: RSC Advances, Vol. 5, No. 18, 2015, p. 13930-13940.

Research output: Contribution to journalArticle

Dhawale, D, Mane, GP, Joseph, S, Talapaneni, SN, Anand, C, Mano, A, Aldeyab, SS, Lakhi, KS & Vinu, A 2015, 'Cobalt oxide functionalized nanoporous carbon electrodes and their excellent supercapacitive performance', RSC Advances, vol. 5, no. 18, pp. 13930-13940. https://doi.org/10.1039/c4ra14041a
Dhawale, Dattatray ; Mane, Gurudas P. ; Joseph, Stalin ; Talapaneni, Siddulu N. ; Anand, Chokkalingam ; Mano, Ajayan ; Aldeyab, Salem S. ; Lakhi, Kripal S. ; Vinu, Ajayan. / Cobalt oxide functionalized nanoporous carbon electrodes and their excellent supercapacitive performance. In: RSC Advances. 2015 ; Vol. 5, No. 18. pp. 13930-13940.
@article{21ea882a8280441499e9212a6b5d4001,
title = "Cobalt oxide functionalized nanoporous carbon electrodes and their excellent supercapacitive performance",
abstract = "Nanoporous carbon (CMK-3-150) functionalized with different amounts of cobalt oxide (CoO) nanoparticles was synthesized by an incipient wetness impregnation technique for supercapacitor application. The characterization results reveal that the specific surface area and pore volume of the CoO functionalized CMK-3-150 marginally decrease upon increasing the amount of the CoO whereas the pore diameter and the structure of the CMK-3-150 were not affected even after the functionalization. The electrochemical measurements show that the specific capacitance of the electrodes was enhanced after the functionalization with CoO. Among the electrodes studied, CMK-3-150 functionalized with 15 wt{\%} CoO shows an excellent cycling stability and specific capacitance of 331 F g-1, which is ca. two times higher than that of the pure nanoporous carbon. This enhanced performance is due to the combined contribution of electrical double layer capacitance and pseudocapacitance. A symmetric supercapacitor device based on the CMK-3-150-15Co electrode gives the maximum energy density of 29.67 W h kg-1 at a power density of 0.07 kW kg-1. This journal is",
author = "Dattatray Dhawale and Mane, {Gurudas P.} and Stalin Joseph and Talapaneni, {Siddulu N.} and Chokkalingam Anand and Ajayan Mano and Aldeyab, {Salem S.} and Lakhi, {Kripal S.} and Ajayan Vinu",
year = "2015",
doi = "10.1039/c4ra14041a",
language = "English",
volume = "5",
pages = "13930--13940",
journal = "RSC Advances",
issn = "2046-2069",
publisher = "Royal Society of Chemistry",
number = "18",

}

TY - JOUR

T1 - Cobalt oxide functionalized nanoporous carbon electrodes and their excellent supercapacitive performance

AU - Dhawale, Dattatray

AU - Mane, Gurudas P.

AU - Joseph, Stalin

AU - Talapaneni, Siddulu N.

AU - Anand, Chokkalingam

AU - Mano, Ajayan

AU - Aldeyab, Salem S.

AU - Lakhi, Kripal S.

AU - Vinu, Ajayan

PY - 2015

Y1 - 2015

N2 - Nanoporous carbon (CMK-3-150) functionalized with different amounts of cobalt oxide (CoO) nanoparticles was synthesized by an incipient wetness impregnation technique for supercapacitor application. The characterization results reveal that the specific surface area and pore volume of the CoO functionalized CMK-3-150 marginally decrease upon increasing the amount of the CoO whereas the pore diameter and the structure of the CMK-3-150 were not affected even after the functionalization. The electrochemical measurements show that the specific capacitance of the electrodes was enhanced after the functionalization with CoO. Among the electrodes studied, CMK-3-150 functionalized with 15 wt% CoO shows an excellent cycling stability and specific capacitance of 331 F g-1, which is ca. two times higher than that of the pure nanoporous carbon. This enhanced performance is due to the combined contribution of electrical double layer capacitance and pseudocapacitance. A symmetric supercapacitor device based on the CMK-3-150-15Co electrode gives the maximum energy density of 29.67 W h kg-1 at a power density of 0.07 kW kg-1. This journal is

AB - Nanoporous carbon (CMK-3-150) functionalized with different amounts of cobalt oxide (CoO) nanoparticles was synthesized by an incipient wetness impregnation technique for supercapacitor application. The characterization results reveal that the specific surface area and pore volume of the CoO functionalized CMK-3-150 marginally decrease upon increasing the amount of the CoO whereas the pore diameter and the structure of the CMK-3-150 were not affected even after the functionalization. The electrochemical measurements show that the specific capacitance of the electrodes was enhanced after the functionalization with CoO. Among the electrodes studied, CMK-3-150 functionalized with 15 wt% CoO shows an excellent cycling stability and specific capacitance of 331 F g-1, which is ca. two times higher than that of the pure nanoporous carbon. This enhanced performance is due to the combined contribution of electrical double layer capacitance and pseudocapacitance. A symmetric supercapacitor device based on the CMK-3-150-15Co electrode gives the maximum energy density of 29.67 W h kg-1 at a power density of 0.07 kW kg-1. This journal is

UR - http://www.scopus.com/inward/record.url?scp=84922566630&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84922566630&partnerID=8YFLogxK

U2 - 10.1039/c4ra14041a

DO - 10.1039/c4ra14041a

M3 - Article

VL - 5

SP - 13930

EP - 13940

JO - RSC Advances

JF - RSC Advances

SN - 2046-2069

IS - 18

ER -