Aging evaluation of asphalt samples with Low Field Nuclear Magnetic Resonance

Ilaria Menapace, Marcel Nogueira d'Eurydice, Petrik Galvosas, Mark W. Hunter, Okan Sirin, Eyad Masad

Research output: Contribution to journalArticle

8 Citations (Scopus)

Abstract

In this study, a recently developed methodology to assess aging of pavements by using Low Field Nuclear Magnetic Resonance (LF-NMR) was applied to asphalt mix samples at different aging states. The ultimate objective of this method is to monitor the long-term aging of asphalt binder in mixture cores without binder extraction. The asphalt samples were long-term aged at 70 °C for different durations. At the end of this process, specimens were heated again to 70 °C and measured in the LF-NMR while cooling to room temperature. Lower cumulative amplitudes were found in samples that were aged for longer durations. An NMR probe that can detect shorter transverse relaxation times T2 was used in order to increase the accuracy of the method. The unaged asphalt binder was measured as temperature dropped from 80 to 40 °C and it was observed that the cumulative amplitude was fairly constant throughout the process. The corresponding change in the binder viscosity was expressed by the T2 shifts to shorter times. This means that the faster NMR probe was capable to minimize the NMR signal losses and therefore it is a suitable tool to investigate asphalt samples. Asphalt binders were extracted from the aged samples and subjected to LF-NMR measurements with the fast NMR probe. It was possible to detect aging trends in the binders, which were in agreement with viscosity trends measured with the Dynamic Shear Rheometer (DSR). The differences in the cumulative amplitude among binders with different aging states mainly depend on the hydrogen nuclei to weight ratio (chemistry) and less on the temperature and measurable limit of the NMR device. This improves the accuracy of the method in the estimation of the binder aging state. In addition, the employed aggregates were separately investigated using LF-NMR.

Original languageEnglish
Pages (from-to)165-175
Number of pages11
JournalMaterials Characterization
Volume128
DOIs
Publication statusPublished - 1 Jun 2017

Fingerprint

asphalt
Asphalt
Binders
Aging of materials
Nuclear magnetic resonance
nuclear magnetic resonance
evaluation
probes
Viscosity
Magnetic resonance measurement
viscosity
trends
pavements
rheometers
Rheometers

Keywords

  • Aging
  • Asphalt
  • Low Field Nuclear Magnetic Resonance
  • Relative Hydrogen Index
  • Viscosity

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Cite this

Aging evaluation of asphalt samples with Low Field Nuclear Magnetic Resonance. / Menapace, Ilaria; Nogueira d'Eurydice, Marcel; Galvosas, Petrik; Hunter, Mark W.; Sirin, Okan; Masad, Eyad.

In: Materials Characterization, Vol. 128, 01.06.2017, p. 165-175.

Research output: Contribution to journalArticle

Menapace, I, Nogueira d'Eurydice, M, Galvosas, P, Hunter, MW, Sirin, O & Masad, E 2017, 'Aging evaluation of asphalt samples with Low Field Nuclear Magnetic Resonance', Materials Characterization, vol. 128, pp. 165-175. https://doi.org/10.1016/j.matchar.2017.01.029
Menapace, Ilaria ; Nogueira d'Eurydice, Marcel ; Galvosas, Petrik ; Hunter, Mark W. ; Sirin, Okan ; Masad, Eyad. / Aging evaluation of asphalt samples with Low Field Nuclear Magnetic Resonance. In: Materials Characterization. 2017 ; Vol. 128. pp. 165-175.
@article{7b80196af3424d4089385300f6386889,
title = "Aging evaluation of asphalt samples with Low Field Nuclear Magnetic Resonance",
abstract = "In this study, a recently developed methodology to assess aging of pavements by using Low Field Nuclear Magnetic Resonance (LF-NMR) was applied to asphalt mix samples at different aging states. The ultimate objective of this method is to monitor the long-term aging of asphalt binder in mixture cores without binder extraction. The asphalt samples were long-term aged at 70 °C for different durations. At the end of this process, specimens were heated again to 70 °C and measured in the LF-NMR while cooling to room temperature. Lower cumulative amplitudes were found in samples that were aged for longer durations. An NMR probe that can detect shorter transverse relaxation times T2 was used in order to increase the accuracy of the method. The unaged asphalt binder was measured as temperature dropped from 80 to 40 °C and it was observed that the cumulative amplitude was fairly constant throughout the process. The corresponding change in the binder viscosity was expressed by the T2 shifts to shorter times. This means that the faster NMR probe was capable to minimize the NMR signal losses and therefore it is a suitable tool to investigate asphalt samples. Asphalt binders were extracted from the aged samples and subjected to LF-NMR measurements with the fast NMR probe. It was possible to detect aging trends in the binders, which were in agreement with viscosity trends measured with the Dynamic Shear Rheometer (DSR). The differences in the cumulative amplitude among binders with different aging states mainly depend on the hydrogen nuclei to weight ratio (chemistry) and less on the temperature and measurable limit of the NMR device. This improves the accuracy of the method in the estimation of the binder aging state. In addition, the employed aggregates were separately investigated using LF-NMR.",
keywords = "Aging, Asphalt, Low Field Nuclear Magnetic Resonance, Relative Hydrogen Index, Viscosity",
author = "Ilaria Menapace and {Nogueira d'Eurydice}, Marcel and Petrik Galvosas and Hunter, {Mark W.} and Okan Sirin and Eyad Masad",
year = "2017",
month = "6",
day = "1",
doi = "10.1016/j.matchar.2017.01.029",
language = "English",
volume = "128",
pages = "165--175",
journal = "Materials Characterization",
issn = "1044-5803",
publisher = "Elsevier Inc.",

}

TY - JOUR

T1 - Aging evaluation of asphalt samples with Low Field Nuclear Magnetic Resonance

AU - Menapace, Ilaria

AU - Nogueira d'Eurydice, Marcel

AU - Galvosas, Petrik

AU - Hunter, Mark W.

AU - Sirin, Okan

AU - Masad, Eyad

PY - 2017/6/1

Y1 - 2017/6/1

N2 - In this study, a recently developed methodology to assess aging of pavements by using Low Field Nuclear Magnetic Resonance (LF-NMR) was applied to asphalt mix samples at different aging states. The ultimate objective of this method is to monitor the long-term aging of asphalt binder in mixture cores without binder extraction. The asphalt samples were long-term aged at 70 °C for different durations. At the end of this process, specimens were heated again to 70 °C and measured in the LF-NMR while cooling to room temperature. Lower cumulative amplitudes were found in samples that were aged for longer durations. An NMR probe that can detect shorter transverse relaxation times T2 was used in order to increase the accuracy of the method. The unaged asphalt binder was measured as temperature dropped from 80 to 40 °C and it was observed that the cumulative amplitude was fairly constant throughout the process. The corresponding change in the binder viscosity was expressed by the T2 shifts to shorter times. This means that the faster NMR probe was capable to minimize the NMR signal losses and therefore it is a suitable tool to investigate asphalt samples. Asphalt binders were extracted from the aged samples and subjected to LF-NMR measurements with the fast NMR probe. It was possible to detect aging trends in the binders, which were in agreement with viscosity trends measured with the Dynamic Shear Rheometer (DSR). The differences in the cumulative amplitude among binders with different aging states mainly depend on the hydrogen nuclei to weight ratio (chemistry) and less on the temperature and measurable limit of the NMR device. This improves the accuracy of the method in the estimation of the binder aging state. In addition, the employed aggregates were separately investigated using LF-NMR.

AB - In this study, a recently developed methodology to assess aging of pavements by using Low Field Nuclear Magnetic Resonance (LF-NMR) was applied to asphalt mix samples at different aging states. The ultimate objective of this method is to monitor the long-term aging of asphalt binder in mixture cores without binder extraction. The asphalt samples were long-term aged at 70 °C for different durations. At the end of this process, specimens were heated again to 70 °C and measured in the LF-NMR while cooling to room temperature. Lower cumulative amplitudes were found in samples that were aged for longer durations. An NMR probe that can detect shorter transverse relaxation times T2 was used in order to increase the accuracy of the method. The unaged asphalt binder was measured as temperature dropped from 80 to 40 °C and it was observed that the cumulative amplitude was fairly constant throughout the process. The corresponding change in the binder viscosity was expressed by the T2 shifts to shorter times. This means that the faster NMR probe was capable to minimize the NMR signal losses and therefore it is a suitable tool to investigate asphalt samples. Asphalt binders were extracted from the aged samples and subjected to LF-NMR measurements with the fast NMR probe. It was possible to detect aging trends in the binders, which were in agreement with viscosity trends measured with the Dynamic Shear Rheometer (DSR). The differences in the cumulative amplitude among binders with different aging states mainly depend on the hydrogen nuclei to weight ratio (chemistry) and less on the temperature and measurable limit of the NMR device. This improves the accuracy of the method in the estimation of the binder aging state. In addition, the employed aggregates were separately investigated using LF-NMR.

KW - Aging

KW - Asphalt

KW - Low Field Nuclear Magnetic Resonance

KW - Relative Hydrogen Index

KW - Viscosity

UR - http://www.scopus.com/inward/record.url?scp=85016987732&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85016987732&partnerID=8YFLogxK

U2 - 10.1016/j.matchar.2017.01.029

DO - 10.1016/j.matchar.2017.01.029

M3 - Article

AN - SCOPUS:85016987732

VL - 128

SP - 165

EP - 175

JO - Materials Characterization

JF - Materials Characterization

SN - 1044-5803

ER -